Property | Test Method | Typical Value, Units |
|
Film Properties |
|
Thickness of Film Tested | D 374 | 264 Microns (10.4 mils) |
Intrinsic Viscosity | | (film) | EMN-A-AC-G-V-1 | 0.788 |
Haze | D 1003 | 0.71 % |
Gloss | | @ 60° | D 2457 | 149 |
Transparency | D 1746 | 100 % |
Regular Transmittance | D 1003 | 89 % |
Total Transmittance | D 1003 | 92 % |
Water Vapor Transmission Rated | F 372 | 6.8 g/m2·24h (0.4 g/100in.2·24h) |
Gas Permeability, CO2 | D 1434 | 25.6 cm3·mm/m2·24h·atm (64 cm3·mil/100in.2·24h·atm) |
Gas Permeability, O2g | D 3985 | 5.2 cm3·mm/m2·24h·atm (12 cm3·mil/100in.2·24h·atm) |
Elmendorf Tear Resistance | | M.D. | D 1922 | 3538 g/mm (957 gf) |
T.D. | D 1922 | 5063 g/mm (1395 gf) |
PPT Tear Resistance | | M.D. | D 2582 | 95.4 N (21.4 lbf) |
T.D. | D 2582 | 116.5 N (26.2 lbf) |
Tear Propagation Resistance, Split Tear Method | | @ 254 mm/min (10 in./min) M.D. | D 1938 | 60.5 N/mm (345 lbf/in.) |
@ 254 mm/min (10 in./min) T.D. | D 1938 | 83.3 N/mm (476 lbf/in.) |
Tear Resistance, Trouser @ 200 mm/min | | M.D. | ISO 6383-1 | 73.3 N/mm |
T.D. | ISO 6383-1 | 94.1 N/mm |
Tensile Strength @ Yield | | M.D. | D 882 | 53.7 MPa (7789 psi) |
T.D. | D 882 | 47.9 MPa (6947 psi) |
Tensile Strength @ Break | | M.D. | D 882 | 51.5 MPa (7469 psi) |
T.D. | D 882 | 46.7 MPa (6773 psi) |
Elongation @ Yield | | M.D. | D 882 | 5.8 % |
T.D. | D 882 | 4.7 % |
Elongation @ Break | | M.D. | D 882 | 444 % |
T.D. | D 882 | 557 % |
Tensile Modulus | | M.D. | D 882 | 2140 MPa (3.10 x 105 psi) |
T.D. | D 882 | 2153 MPa (3.12 x 105 psi) |
Dart Impacth | | @ -18°C (0°F) | D 1709A Modified | 373 g |
@ 23°C (73°F) | D 1709A Modified | 446 g |
Injection Molded Properties (ASTM Method) |
|
Specific Gravity | D 792 | 1.3286 |
Tensile Stress @ Break | D 638 | 24.7 MPa (3582 psi) |
Tensile Stress @ Yield | D 638 | 56.3 MPa (8166 psi) |
Tensile Modulus | D 638 | 2390 MPa (3.5 x 105 psi) |
Flexural Modulus | D 790 | 2301 MPa (3.3 x 105 psi) |
Flexural Yield Strength | D 790 | 74.7 MPa (10831 psi) |
Deflection Temperature | | @ 0.455 MPa (66 psi) | D 648 | 67.7 °C |
@ 1.82 MPa (264 psi) | D 648 | 61.4 °C |
Rockwell Hardness, R Scale | D 785 | 111 |
Izod Impact Strength, Notched | | @ 23°C (73°F) | D 256 | 66.03 J/m |
@ -40°C (-40°F) | D 256 | 39.59 J/m |
Impact Strength, Unnotchedf | | @ -20°C (-4°F) | D 4812 | NB |
@ 23°C (73°F) | D 4812 | NB |
@ -30°C (-22°F) | D 4812 | NB |
@ -40°C (-40°F) | D 4812 | 2911.33 J/m |
Impact Resistance (Puncture), Energy @ Max. Load | | 2.5-mm (0.100-in.) Thick Plaques, @ 23°C (73°F) | D 3763 | 33.4 J |
2.5-mm (0.100-in.) Thick Plaques, @ -40°C (-40°F) | D 3763 | 4.23 J |
3.2-mm (0.125-in.) Thick Plaques @ 23°C (73°F) | D 3763 | 34.27 J |
3.2-mm (0.125-in.) Thick Plaques @ -40°C (-40°F) | D 3763 | 3.72 J |
Injection Molded Properties (ISO Method) |
|
Tensile Stress @ Break | ISO 527 | 25.1 MPa |
Tensile Stress @ Yield | ISO 527 | 56.2 MPa |
Tensile Modulus | ISO 527 | 2401 MPa |
Flexural Modulus | ISO 178 | 2334 MPa |
Flexural Yield Strength | ISO 178 | 82.3 MPa |
Deflection Temperature | | @ 0.45 MPa | ISO 75 | 66.2 °C |
@ 1.80 MPa | ISO 75 | 61.1 °C |
Izod Impact Strength, Notched, Type 1 Specimen, Type A Notch | | @ 23°C | ISO 180 | 6.24 kJ/m2 |
@ -40°C | ISO 180 | 3.71 kJ/m2 |
Impact Strength, Unnotched, Type 1 Specimenc | | @ -20°C | ISO 180 | NB kJ/m2 |
@ 23°C | ISO 180 | NB kJ/m2 |
@ -30°C | ISO 180 | 266.56 kJ/m2 |
@ -40°C | ISO 180 | 248.41 kJ/m2 |
Impact Resistance (Puncture), Energy @ Max. Loade | | 2.5-mm Thick Plaques @ 23°C | ISO 6603-2 | 38.93 J |
2.5-mm Thick Plaques @ -40°C | ISO 6603-2 | 3.44 J |
3.2-mm Thick Plaques @ 23°C | ISO 6603-2 | 38.04 J |
3.2-mm Thick Plaques @ -40°C | ISO 6603-2 | 2.36 J |
Pellet Properties |
|
Crystalline Density | D 1505 | 1.4 g/cm3 |
Bulk Density | | Poured | D 1895 | 850 kg/m3 (53 lb/ft3) |
Vibrated | | 911 kg/m3 (57 lb/ft3) |
Melt Density | | @ 285°C (545°F) | D 1238 (Note A- Table 2) | 1.1 g/cm3 |
Crystalline Peak Melting Point (Tm)a | D 3418 | 238°C-461°F |
Heat of Fusionb | E 793 | 60 kJ/kg (14 cal/g) |
Specific Heatb | | @ 100°C (212°F) | E 1269 | 1.5 kJ/kg·K (0.35 Btu/lb·°F) |
@ 200°C (392°F) | E 1269 | 1.8 kJ/kg·K (0.43 Btu/lb·°F) |
@ 23°C (73°F) | E 1269 | 1.1 kJ/kg·K (0.27 Btu/lb·°F) |
@ 280°C (536°F) | E 1269 | 2.0 kJ/kg·K (0.48 Btu/lb·°F) |
@ 80°C (176°F) | E 1269 | 1.4 kJ/kg·K (0.33 Btu/lb·°F) |
Pellet Size | | 3.27 mm (0.1 in.) |
Pellet Shape | | Cubical |
|