Technical Data Sheet
Eastman Tritan™ Copolyester VX351HF
Applications
Eyewear
Key Attributes
Ease of processing
Excellent clarity
Excellent hydrolytic stability
Outstanding impact resistance
Quick cycle times
Superior chemical resistance
Product Description
Tritan VX351HF is an amorphous copolyester with excellent clarity and impact resistance. The outstanding chemical resistance, hydrolytic stability, and ease of processing make Tritan™ VX351HF an ideal candidate for a broad spectrum of optical applications such sunglass lenses, optical glass lenses and safety eyewear.
Typical Properties
Property
a
Test Method
b
Typical Value, Units
c
General Properties (ASTM Method)
Specific Gravity
D 792
1.18
Mold Shrinkage
D 955
0.005-0.007 mm/mm (0.005-0.007 in./in.)
General Properties (ISO Method)
Density
ISO 1183, Method D
1.18 g/cm
3
Mechanical Properties (ASTM Method)
Tensile Stress @ Yield
D 638
43 MPa (6200 psi)
Tensile Stress @ Break
D 638
52 MPa (7500 psi)
Elongation @ Yield
D 638
7 %
Elongation @ Break
D 638
210 %
Tensile Modulus
D 638
1575 MPa (2.28 x 10
5
psi)
Flexural Modulus
D 790
1575 MPa (2.28 x 10
5
psi)
Flexural Yield Strength
D 790
64 MPa (9300 psi)
Rockwell Hardness, R Scale
D 785
111
Izod Impact Strength, Notched
@ 23°C (73°F)
D 256
860 J/m (16.1 ft·lbf/in.)
@ -40°C (-40°F)
D 256
110 J/m (2.1 ft·lbf/in.)
Impact Strength, Unnotched
@ 23°C (73°F)
D 4812
NB
@ -40°C (-40°F)
D 4812
NB
Impact Resistance (Puncture), Energy @ Max. Load
@ 23°C (73°F)
D 3763
53 J (39 ft·lbf)
@ -40°C (-40°F)
D 3763
57 J (42 ft·lbf)
Mechanical Properties (ISO Method)
Tensile Strength @ Yield
ISO 527
43 MPa
Tensile Stress @ Break
ISO 527
53 MPa
Elongation @ Yield
ISO 527
6 %
Elongation @ Break
ISO 527
160 %
Tensile Modulus
ISO 527
1620 MPa
Flexural Modulus
ISO 527
1590 MPa
Flexural Yield Strength
ISO 178
62 MPa
Izod Impact Strength, Notched
@ 23°C
ISO 180
85 kJ/m
2
@ -40°C
ISO 180
11 kJ/m
2
Optical Properties (ASTM Method)
Haze
D 1003
<0.40 %
Total Transmittance
D 1003
91 %
Refractive Index
d
C 1648
1.5651
ABBE Number
d
C 1648
31.07
Thermal Properties (ASTM Method)
Deflection Temperature
@ 0.455 MPa (66 psi)
D 648
94 °C (201 °F)
@ 1.82 MPa (264 psi)
D 648
81 °C (178 °F)
Typical Processing Conditions
Drying Temperature
88 °C (190 °F)
Drying Time
4-6 hrs
Processing Melt Temperature
260-282 °C (500-540 °F)
Mold Temperature
38-66 °C (100-150 °F)
a
Unless noted otherwise, all tests are run at 23°C (73°F) and 50% relative humidity.
b
Unless noted otherwise, the test method is ASTM.
c
Units are in SI or US customary units.
d
Measurements made on 5 mil extruded film.
Technical Disclaimer
Eastman makes no representation and disclaims any warranty that the material in any particular shipment will conform exactly to the values given. Values as well as the performance of the final molded article may be affected by various factors such as the part design, mold design or tooling, drying, processing conditions as well as coloring or pigmentation of the product. No warranty of merchantability or fitness for use is made, and nothing herein waives any of the Seller''''''''s conditions of sale. You must make your own determination of the suitability of this product in your specific application due to the many factors (e.g. design, processing and conditions of use) that affect the performance of the final molded article. Suitability of use should be evaluated with appropriate testing and analysis. The processing melt temperature and mold temperature refer to the actual resin melt temperature and actual mold surface temperature respectively. Consider overall resin residence time, part shot size utilization and part geometry to set appropriate processing melt temperature and mold temperature in order to minimize IV loss and maximize molded part performance.
Comments
Properties reported here are based on limited testing. Eastman makes no representation that the material in any particular shipment will conform exactly to the values given.
Eastman and its marketing affiliates shall not be responsible for the use of this information, or of any product, method, or apparatus mentioned, and you must make your own determination of its suitability and completeness for your own use, for the protection of the environment, and for the health and safety of your employees and purchasers of your products. No warranty is made of the merchantability of fitness of any product, and nothing herein waives any of the Seller's conditions of sale.
8/21/2023 10:49:34 AM