Technical Data Sheet
Eastman TREVA™ Renew Engineering Bioplastic OP6026-71 Clear
Applications
Eyewear
Key Attributes
Dimensional stability
Easy polish and paint
Excellent flow
Warm touch and feel
Product Description
Eastman TREVA™ Renew engineering bioplastic OP6026-71 Clear is a new cellulose-based engineering bioplastic that offers both high performance and reduced environmental impact. Renew polymers enable a brand to reduce consumption of fossil feedstock-based plastics, achieve sustainability targets without compromise, and be a fast mover in a growing market for sustainable consumer products.
TREVA™ is chemically resistant, dimensionally stable, flows well, and has excellent flow, BPA-free and has low birefringence.
Eastman Renew polymers have been certified by International Sustainability & Carbon Certification (ISCC), a global, independent agency for tracking sustainable content in a variety of industries. Renew polymers are produced with ISCC certified circular content by mass balance allocation.
Typical Properties
Property
a
Test Method
b
Typical Value, Units
c
General Properties
Bio-based Content
48 Mass %
Specific Gravity
D 792
1.22
Mechanical Properties
Tensile Stress @ Yield
D 638
49 MPa (7107 psi)
Tensile Stress @ Break
D 638
48 MPa (6962 psi)
Elongation @ Break
D 638
18 %
Flexural Modulus
D 790
1940 MPa (2.81 x 10
5
psi)
Rockwell Hardness, R Scale
D 785
100
Izod Impact Strength, Notched
@ 23°C (73°F)
D 256
216 J/m (4.05 ft·lbf/in.)
@ -40°C (-40°F)
D 256
100 J/m (1.87 ft·lbf/in.)
Miscellaneous Properties
Mold Shrinkage, normal
D 955
0.7 %
Permanence Properties
Water Absorption, 24 h immersion
D 570
2.3 %
Target Processing Conditions
Drying Temperature in a Desiccant Dryer
75 °C (170 °F)
Drying Time in a Desiccant Dryer
4 hours
Barrel Set Temperature
e
235 °C (455 °F)
Mold Temperature
85 °C (185 °F)
Injection Speed
30 mm/sec (1.2 in./sec)
Maximum Barrel Residence Time
4 minutes
Thermal Properties
Deflection Temperature
d
@ 0.455 MPa (66 psi)
D 648
114 °C (238 °F)
@ 1.82 MPa (264 psi)
D 648
99 °C (210 °F)
Vicat Softening Temperature
d
D 1525
135 °C (275 °F)
a
Unless noted otherwise, all tests are run at 23°C (73°F) and 50% relative humidity.
b
Unless noted otherwise, the test method is ASTM.
c
Units are in SI or US customary units.
d
Conditioned 4 hours at 70°C (158°F).
e
With actual measured melt temperature not to exceed 260°C (500°F).
Comments
Properties reported here are typical of average lots. Eastman makes no representation that the material in any particular shipment will conform exactly to the values given.
Eastman and its marketing affiliates shall not be responsible for the use of this information, or of any product, method, or apparatus mentioned, and you must make your own determination of its suitability and completeness for your own use, for the protection of the environment, and for the health and safety of your employees and purchasers of your products. No warranty is made of the merchantability of fitness of any product, and nothing herein waives any of the Seller's conditions of sale.