Technical Data Sheet
Tenite™ Butyrate 264E4861310 Clear Trsp


Applications
  • Compounders
  • Equipment & machinery
  • Outdoor signs
  • Sporting equipment

Product Description
Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite cellulosic plastics are available in natural, clear, selected ambers, or smoke transparents and black translucent. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite Cellulose Acetate Butyrate 264-10 has a plasticizer level of 10%.

Typical Properties

PropertyaTest MethodbTypical Value, Unitsc
General
Plasticizer 10 %
Specific GravityD 7921.19
Mechanical Properties
Tensile Stress @ YieldD 63833.1 MPa (4800 psi)
Tensile Stress @ BreakD 63843.4 MPa (6300 psi)
Elongation @ BreakD 63850 %
Flexural ModulusD 7901379 MPa (2.00 x 105 psi)
Flexural Yield StrengthD 79045.5 MPa (6600 psi)
Rockwell Hardness, R ScaleD 78578
Izod Impact Strength, Notched 
     @ 23°C (73°F)D 256240 J/m (4.5 ft·lbf/in.)
     @ -40°C (-40°F)D 25696 J/m (1.8 ft·lbf/in.)
Miscellaneous Butyrate Properties
Refractive Index, nDD 5421.46-1.49
Light TransmissioneE 308>90 %
HazeeD 1003<8.5 %
Specific Heat 
     @ 23°C (73°F)DSC1.26-1.67 kJ/kg·K (0.301-0.399 Btu/lb·°F)
Thermal ConductivityC 1770.17-0.33 W/m·K (1.2-2.3 Btu·in./h·ft2·°F)
Coefficient of Linear Thermal ExpansionD 69611-17 x 10-5 /°C (mm/mm·°C) (6-9 x 10-5 /°F (in./in.·°F))
Mold ShrinkageD 9550.2-0.6 %
Dielectric StrengthD 14911.8-18.7 kV/mm (300-475 V/mil)
Dielectric Constant 
     1 MHzD 1503.3-3.8
Dissipation Factor 
     1 MHzD 1500.01-0.15
Volume ResistivityD 2571013-1015 ohm·cm
Permanence Properties
Water Absorption, 24 h immersionD 5701.4 %
Soluble Matter LossD 5700.1 %
Weight Loss on Heating 
     [72 hours @ 80°C (176°F)]D 7070.5 %
Thermal Properties
Deflection Temperatured 
     @ 0.455 MPa (66 psi)D 64885 °C (185 °F)
     @ 1.82 MPa (264 psi)D 64874 °C (165 °F)
Vicat Softening TemperaturedD 1525104 °C (219 °F)

aUnless noted otherwise, all tests are run at 23°C (73°F) and 50% relative humidity.
bUnless noted otherwise, the test method is ASTM.
cUnits are in SI or US customary units.
dConditioned 4 hours @ 70°C (158°F)
e1.52-mm (0.06-in.) specimen thickness



Comments
Properties reported here are typical of average lots. Eastman makes no representation that the material in any particular shipment will conform exactly to the values given.


Eastman and its marketing affiliates shall not be responsible for the use of this information, or of any product, method, or apparatus mentioned, and you must make your own determination of its suitability and completeness for your own use, for the protection of the environment, and for the health and safety of your employees and purchasers of your products. No warranty is made of the merchantability of fitness of any product, and nothing herein waives any of the Seller's conditions of sale.