Tenite™ Propionate 360E0096914 Natural Trsp


Applications
  • Consumer housewares-NFC
  • Diffuser film
  • Medical devices
  • Profiles

Product Description
Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite cellulosic plastics are available in natural, clear, selected ambers or smoke transparents and black translucent. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite cellulosic acetate propionate 360-14 has a plasticizer level of 14%.

Typical Properties

PropertyaTest MethodbTypical Value, Unitsc
General
Plasticizer 14 %
Specific GravityD 7921.2
Mechanical Properties
Tensile Stress @ YieldD 63829.3 MPa (4300 psi)
Tensile Stress @ BreakD 63831.7 MPa (4600 psi)
Elongation @ BreakD 63845 %
Flexural ModulusD 7901345 MPa (1.95 x 105 psi)
Flexural Yield StrengthD 79038.3 MPa (5600 psi)
Rockwell Hardness, R ScaleD 78573
Izod Impact Strength, Notched 
     @ 23°C (73°F)D 256475 J/m (8.9 ft·lbf/in.)
     @ -40°C (-40°F)D 256115 J/m (2.2 ft·lbf/in.)
Miscellaneous Propionate Properties
Refractive Index, nDD 5421.46-1.49
Light TransmissioneE 308>90 %
HazeeD 1003<8.5 %
Specific Heat 
     @ 23°C (73°F)DSC1.26-1.67 kJ/kg·K (0.301-0.399 Btu/lb·°F)
Thermal ConductivityC 1770.17-0.33 W/m·K (1.2-2.3 Btu·in./h·ft2·°F)
Coefficient of Linear Thermal ExpansionD 69611-17 x 10-5 /°C (mm/mm·°C) (6-9 x 10-5 /°F (in./in.·°F))
Mold ShrinkageD 9550.2-0.6 %
Dielectric StrengthD 14911.8-18.7 kV/mm (300-475 V/mil)
Dielectric Constant 
     1 MHzD 1503.3-3.8
Dissipation Factor 
     1 MHzD 1500.01-0.15
Volume ResistivityD 2571013-1015 ohm·cm
Permanence Properties
Water Absorption, 24 h immersionD 5701.5 %
Soluble Matter LossD 5700.1 %
Weight Loss on Heating 
     [72 hours @ 80°C (176°F)]D 15620.9 %
Thermal Properties
Deflection Temperatured 
     @ 0.455 MPa (66 psi)D 64882 °C (179 °F)
     @ 1.82 MPa (264 psi)D 64874 °C (165 °F)
Vicat Softening TemperaturedD 152594 °C (202 °F)

aUnless noted otherwise, all tests are run at 23°C (73°F) and 50% relative humidity.
bUnless noted otherwise, the test method is ASTM.
cUnits are in SI or US customary units.
dConditioned 4 hours @ 70°C (158°F)
e1.52-mm (0.06 in.) thickness



Comments
Properties reported here are typical of average lots. Eastman makes no representation that the material in any particular shipment will conform exactly to the values given.


Eastman and its marketing affiliates shall not be responsible for the use of this information, or of any product, method, or apparatus mentioned, and you must make your own determination of its suitability and completeness for your own use, for the protection of the environment, and for the health and safety of your employees and purchasers of your products. No warranty is made of the merchantability of fitness of any product, and nothing herein waives any of the Seller's conditions of sale.


12/14/2023 4:22:47 PM