Technical Data Sheet
Tenite™ Renew Propionate 380A4000010 Clear Trsp - 68
Industrial machine guards
Large appliances non-food contact
Small appliances non-food contact
Tenite™ Renew cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite Renew cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite Renew cellulosic plastics are available in natural, clear, selected ambers or smoke transparent and black translucent. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite Renew Cellulose Acetate Propionate 380-10 has a plasticizer level of 10%. It is resistant to high temperatures.
Eastman Renew polymers have been certified by International Sustainability & Carbon Certification (ISCC), a global, independent agency for tracking sustainable content in a variety of industries. Renew polymers are produced with ISCC certified circular content by mass balance allocation.
Renew polymers enable a brand to reduce consumption of fossil feedstock-based plastics, achieve sustainability targets without compromise, and be a fast mover in a growing market for sustainable consumer products.
Typical Value, Units
Tensile Stress @ Yield
37.2 MPa (5400 psi)
Tensile Stress @ Break
37.9 MPa (5500 psi)
Elongation @ Break
1724 MPa (2.50 x 10
Flexural Yield Strength
48.3 MPa (7000 psi)
Rockwell Hardness, R Scale
Izod Impact Strength, Notched
@ 23°C (73°F)
304 J/m (5.7 ft·lbf/in.)
@ -40°C (-40°F)
75 J/m (1.4 ft·lbf/in.)
Miscellaneous Propionate Properties
Refractive Index, n
@ 23°C (73°F)
1.26-1.67 kJ/kg·K (0.301-0.399 Btu/lb·°F)
0.17-0.33 W/m·K (1.2-2.3 Btu·in./h·ft
Coefficient of Linear Thermal Expansion
11-17 x 10
/°C (mm/mm·°C) (6-9 x 10
11.8-18.7 kV/mm (300-475 V/mil)
Water Absorption, 24 h immersion
Soluble Matter Loss
Weight Loss on Heating
[72 hours @ 80°C (176°F)]
@ 0.455 MPa (66 psi)
88 °C (190 °F)
@ 1.82 MPa (264 psi)
80 °C (176 °F)
Vicat Softening Temperature
102 °C (216 °F)
Unless noted otherwise, all tests are run at 23°C (73°F) and 50% relative humidity.
Unless noted otherwise, the test method is ASTM.
Units are in SI or US customary units.
Conditioned 4 hours @ 70°C (158°F)
1.52-mm (0.06-in.) thickness
Formula 380 - base
Properties reported here are typical of average lots. Eastman makes no representation that the material in any particular shipment will conform exactly to the values given.
Eastman and its marketing affiliates shall not be responsible for the use of this information, or of any product, method, or apparatus mentioned, and you must make your own determination of its suitability and completeness for your own use, for the protection of the environment, and for the health and safety of your employees and purchasers of your products. No warranty is made of the merchantability of fitness of any product, and nothing herein waives any of the Seller's conditions of sale.