Technical Data Sheet
Eastman Embrace™ LV Renew-35 copolyester


Chemical Synonym
  • Copolyester
Applications
  • Decorative laminates-cabinetry
  • Decorative laminates-wood
  • Home, garden & automotive packaging
  • Labels non food contact
  • Multi-layer film non food contact
  • Shrink film food contact
  • Shrink film non food contact
Key Attributes
  • Customizable shrink curve
  • Eye-catching 360° graphic capability
  • Greater than 75% ultimate shrinkage
  • Low shrink force
  • Optimal machine direction growth
  • Shrinks to fit contour bottles
  • Sparkling clarity and high gloss
  • Super-high print definition

Product Description
The world's leading shrink film just got better with the introduction of Eastman Embrace™ LV Renew-35 copolyester to the Eastman Embrace™ family of resins. LV stands for LOW shrink force and VERSATILE shrink curve. Living up to its name, it demonstrates its versatility with its ability to be produced with 40 to 50% reduction in shrink force, compared with other polyester shrink films and with a shrink curve that is similar to both PVC and OPS while still maintaining ultimate shrinkage greater than 75%. This versatility is achieved by making changes to the extruders manufacturing process. Eastman Embrace™ LV Renew-35 copolyester emulates all visually satisfying attributes expected from the current Eastman Embrace™ such as high gloss and clarity.

This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED®.
The GREENGUARD INDOOR AIR QUALITY CERTIFIED® Mark is a registered certification mark used under license through the GREENGUARD Environmental Institute (GEI). GEI is an industry-independent, non-profit organization that oversees the GREENGUARD Certification Program. The GREENGUARD Certification Program is an industry independent, third-party testing program for low-emitting products and materials for indoor environments. For more information about GEI and to obtain printable certificates for Eastman™ Copolyesters, visit www.greenguard.org. Choose Eastman Chemical Company under the Manufacturer category and click search to display a list of our products.

This product has received a Platinum level Material Health Certificate from the Cradle to Cradle Products Innovation Institute. A Material Health Certificate is awarded to products that meet the Material Health requirements of the multi-attribute Cradle to Cradle CertifiedTM Product Standard. The Cradle to Cradle Products Innovation Institute is a nonprofit organization that administers the publicly available Cradle to Cradle CertifiedTM Product Standard, which provides designers and manufacturers with criteria and requirements for continually improving product materials and manufacturing processes. The Material Health Certificate provides manufacturers with a trusted way to communicate their efforts to identify and replace chemicals of concern in their products. For more information about Cradle to Cradle certification and to obtain printable certificates for Eastman copolyesters, visit www.c2ccertified.org. Search for Eastman Chemical Company in the Material Health Certificate Registry.

Eastman Renew polymers have been certified by International Sustainability & Carbon Certification (ISCC), a global, independent agency for tracking sustainable content in a variety of industries. Renew polymers are produced with ISCC certified circular content by mass balance allocation.

Renew polymers enable a brand to reduce consumption of fossil feedstock-based plastics, achieve sustainability targets without compromise, and be a fast mover in a growing market for sustainable consumer products.


Typical Properties

PropertyaTest MethodbTypical Value, Unitsc
Film Properties (Extruded/Cast Film)
Inherent ViscosityEMN-A-AC-G-V-10.70
Thickness of Film Tested 250 Microns (10 mils)
DensityD 15051.30 g/cm3
HazeD 10031.4 %
Gloss 
     @ 60°D 2457161
TransparencyD 174699 %
Regular TransmittanceD 100389 %
Total TransmittanceD 100392 %
Water Vapor Transmission RateeF 12496.7 g/m2·24h (0.43 g/100in.2·24h)
Gas Permeability, O2 
     @ 30°C (86°F), 68% RHD 39857.4 cm3·mm/m2·24h·atm (18.9 cm3·mil/100in.2·24h·atm)
Elmendorf Tear Resistance 
     M.D.D 19226.9 N (704 gf)
     T.D.D 19228.5 N (864 gf)
PPT Tear Resistance 
     M.D.D 258247 N (11 lbf)
     T.D.D 258262 N (14 lbf)
Tear Propagation Resistance, Split Tear Method 
     @ 254 mm/min (10 in./min) M.D.D 193834 N/mm (192 lbf/in.)
     @ 254 mm/min (10 in./min) T.D.D 193837 N/mm (210 lbf/in.)
Tensile Strength @ Break 
     M.D.D 88251 MPa (7400 psi)
     T.D.D 88250 MPa (7300 psi)
Elongation @ Break 
     M.D.D 8824 %
     T.D.D 8824 %
Tensile Modulus 
     M.D.D 8821900 MPa (2.8 x 105 psi)
     T.D.D 8821900 MPa (2.8 x 105 psi)
Vicat Softening TemperatureD 152569 °C (156 °F)
Glass Transition Temperature (Tg)D 152569 °C (159 °F)
Film Properties (Stretched Film)
Inherent ViscosityEMN-A-AC-G-V-10.70
Thickness of Film Tested 50 Microns (2 mils)
DensityD 15051.30 g/cm3
Ultimate Shrinkaged 
     @ 90°C 78 %
HazeD 10033.8 %
Gloss 
     @ 60°D 2457110
TransparencyD 174698 %
Regular TransmittanceD 100387 %
Total TransmittanceD 100392 %
Color 
     a*D 22440.02
     b*D 22440.38
     L*D 224495.8
Water Vapor Transmission RateeF 124925 g/m2·24h (1.6 g/100in.2·24h)
Gas Permeability, O2 
     @ 30°C (86°F), 68% RHD 39853.9 cm3·mm/m2·24h·atm (9.9 cm3·mil/100in.2·24h·atm)
Elmendorf Tear Resistance 
     M.D.D 19222.4 N (242 gf)
Tear Propagation Resistance, Split Tear Method 
     @ 254 mm/min (10 in./min) M.D.D 193828 N/mm (160 lbf/in.)
     @ 254 mm/min (10 in./min) T.D.D 19383 N/mm (16 lbf/in.)
Tensile Strength @ Yield 
     M.D.D 88243 MPa (6200 psi)
     T.D.D 882105 MPa (15200 psi)
Elongation @ Yield 
     M.D.D 8823 %
     T.D.D 8824 %
Tensile Strength @ Break 
     M.D.D 88249 MPa (7100 psi)
     T.D.D 882258 MPa (37400 psi)
Elongation @ Break 
     M.D.D 882480 %
     T.D.D 88242 %
Tensile Modulus 
     M.D.D 8822000 MPa (2.9 x 105 psi)
     T.D.D 8825300 MPa (7.7 x 105 psi)
Vicat Softening TemperatureD 152569 °C (156 °F)
Glass Transition Temperature (Tg)D 152569 °C (159 °F)
Surface Tension, Harmonic Mean 
     Dispersive 44 dynes/cm
     Polar 3 dynes/cm
     Total 48 dynes/cm

aUnless noted otherwise, all tests are run at 23°C (73°F) and 50% relative humidity.
bUnless noted otherwise, the test method is ASTM.
cUnits are in SI or US customary units.
dFor films with a stretch ratio of 5x and normal conditions for EMBRACE.
eTest conducted at 38°C (100°F) and 100% relative humidity.



Comments
Properties reported here are based on limited testing. Eastman makes no representation that the material in any particular shipment will conform exactly to the values given.


Eastman and its marketing affiliates shall not be responsible for the use of this information, or of any product, method, or apparatus mentioned, and you must make your own determination of its suitability and completeness for your own use, for the protection of the environment, and for the health and safety of your employees and purchasers of your products. No warranty is made of the merchantability of fitness of any product, and nothing herein waives any of the Seller's conditions of sale.